NM400硬度350HBW～440HBW/NM450硬度410HBW～490HBW
牌号和化学成分（熔炼分析）应符合表1之规定。
表1
NM400硬度350HBW～440HBW/NM450硬度410HBW～490HBW
|
牌号 |
等级 |
化学成分Wt% |
||||||||
|
C |
Si |
Mn |
P |
S |
Mo |
Cr |
Ni |
B |
||
|
WNM360 |
A |
Max 0.20 |
Max 0.60 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.40 |
Max 1.50 |
/ |
Max 0.004 |
|
B |
Max 0.20 |
Max 0.60 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.40 |
Max 1.50 |
Max 0.50 |
Max 0.004 |
|
|
WNM400 |
A |
Max 0.21 |
Max 0.70 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.40 |
Max 1.50 |
/ |
Max 0.004 |
|
B |
Max 0.21 |
Max 0.70 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.40 |
Max 1.50 |
Max 0.80 |
Max 0.004 |
|
|
WNM450 |
A |
Max 0.26 |
Max 0.70 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.50 |
Max 1.50 |
/ |
Max 0.004 |
|
B |
Max 0.26 |
Max 0.70 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.50 |
Max 1.50 |
Max 0.80 |
Max 0.004 |
|
|
WNM500 |
A |
Max 0.32 |
Max 0.70 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.50 |
Max 1.50 |
/ |
Max 0.004 |
|
B |
Max 0.32 |
Max 0.70 |
Max 1.60 |
Max 0.025 |
Max 0.010 |
Max 0.50 |
Max 1.50 |
Max 0.80 |
Max 0.004 |
|
NM400硬度350HBW～440HBW/NM450硬度410HBW～490HBW
5.2 冶炼方法：电炉＋炉外精炼。
5.3 状态：淬火。为保证性能，必要时，钢板可采用低温回火处理。
5.4力学性能
5.4.1钢板力学性能应符合表2的规定。
并在注明下列补充要求可适用。
A1 提供钢板拉伸试验Rp0.2、Rm、A50的实测值。
A2 提供钢板其它温度的纵向冲击试验的实测值AKV），具体试验温度注明。
A3 180°弯曲试验：横向d≥6a（d为弯心直径，a为试样厚度）
5.5 钢板表面质量应符合GB3274之规定。
表2
NM400硬度350HBW～440HBW/NM450硬度410HBW～490HBW
|
钢种 |
等级 |
硬度 (HBW) |
20℃AKV 纵向 J |
|
|
|
||||
|
WNM360 |
A |
320～400 |
提供 |
|
|
B |
320～400 |
≥27 |
|
|
|
WNM400 |
A |
350～440 |
提供 |
|
|
B |
350～440 |
≥27 |
|
|
|
WNM450 |
A |
410～490 |
提供 |
|
|
B |
410～490 |
≥20 |
|
|
|
WNM500 |
A |
450～540 |
提供 |
|
|
B |
450～540 |
≥20 |
|
NM400硬度350HBW～440HBW/NM450硬度410HBW～490HBW